Appliance Design - February 2008 - (Page 49) JOINING In this shaft-to-grinding-stone application, a thin film of zinc alloy bonds the components with a strong mechanical lock. The joining operation is completed in less than a second. As compared to epoxy, the zinc alloy bond eliminates curing time, and the fixturing tool ensures close tolerance, part-to-part consistency. substrate material has progressed more than a few thousands of an inch. While adhesives need a carefully prepared surface for proper bonding, zinc alloy requires little, if any, preparation, as the adhesion properties of zinc alloy are forgiving of substrate impurities. The materials being bonded need only be industrially clean. The molten alloy’s high fluidity fills voids. In fact, such voids can actually improve the mechanical bond as they provide an even greater surface area for adhesion. This high fluidity compensates for the presence of release oils, as well as most coatings and paints that don’t outgas at low temperatures, permitting a strong mechanical bond. Even PTFE presents no obstacle for zinc alloy’s bonding capabilities, even without the application of primers. Zinc alloy’s high fluidity property also contributes to performance when it comes to bonding strength. Stress distributes uniformly throughout the joint, as the molten alloy completely fills the space between the components. The alloy’s shrinkage delivers a shrink-fit adhesion combined with high stiffness and resistance to pull-off forces. The components themselves will fail before the alloy bond breaks. The metallic bond also allows nondestructive testing with X-rays or eddy current methods to verify joint integrity. Zamak 3 zinc alloy is usually the top choice for bonding applications. (Zamak is a trade name for a family of alloys comprising zinc, aluminum, magnesium, and copper.) Zamak 3 alloy contains (by weight) 4 percent aluminum, and a small amount of magnesium. Zamak 5 alloy, which also contains copper, has 15 perwww.applianceDESIGN.com cent greater strength, plus hardness and corrosion protection. These Zamak alloys have a hardness of up to 82 BHN (Brinell), and shear and tensile strengths of 31 kpsi and 41 kpsi, respectively. Zinc alloy also endures harsh environments, thereby delivering long-term service life. The alloy performs well in operating temperatures up to 230 Deg F (110 DegC). Zinc alloy bonds between most materials maintain integrity even when the materials have different coefficients of expansion. Where a component material’s shrinkage differs from the alloy, shrink-to features may be designed to compensate for the differences. The metal bond won’t become brittle or show undue stress at temperatures down to –40 Deg F (-40 DegC). Zinc alloy has excellent corrosion resistance under normal atmospheric conditions, and in many aqueous, industrial and petroleum environments. It resists gases and most solvents, with the exception of strong acids and caustic solutions. alternate joining The Injected Metal Assembly process is suitable for virtually any assembly of small components that can be joined by adhesives, soldering, welding, brazing, or mechanical processes such as staking, press fitting, and crimping. Quality, consistency, and productivity are typically improved, and costs are typically significantly reduced, compared to these other joining methods. Zinc alloy bonding is well suited for brittle and delicate materials. In one application, joining of an aluminum shaft to a glass disc is achieved in seconds, with no deformation or cracking of the delicate material. In another application, where a shaft is joined to a fragile magnet, the two components are held in precise position in the fixturing tool for injection of the zinc alloy bond. Within less than a second, the assembly is ejected from the tool and ready for immediate use in the application. The zinc alloy hub that joins the magnet and shaft can incorporate a functional feature, such as a stop pin. The production rate is over 1,000 units per hour. Alternatively, there is the potential for considerable cost savings when the pre-manufactured shaft can be eliminated. The shaft is formed as it is cast directly to the magnet. The larger volume of injected alloy that forms the shaft slows production to 600 units per hour, but overall cost reduction is realized. In another example, a magnetic bearing, with a 7.62 mm (0.30-in.) diameter, is encased in a cast ring that provides an accurate outside diameter to within 0.013 mm (0.0005-in.). The brittle magnet is neither cracked nor deformed. FisherTech’s Injected Metal Assembly systems are currently used to provide joining of assemblies in a variety of industries, including controls, appliance, electronic, power tool, hardware and telecom. < For more information, enter . . . . . . . . . . . . . . . . . 308 Or email: info@fishertech .com applianceDESIGN February 2008 49 http://www.appliancedesign.com
For optimal viewing of this digital publication, please enable JavaScript and then refresh the page. If you would like to try to load the digital publication without using Flash Player detection, please click here.