Fabric Architecture Specifier's Guide 2019 - 82

82

www.FabricArchitectureMag.com

Weight

Thickness

Tongue Tear

Test Method

Warp, Fill

Roll Width, Usable

Finished
Fabric

Test Method

DIN 53363

800/550 N

DIN 53363

1800/1800 N

126 in (3.2 m)

31 oz/yd2
(1050 gsm)

12.4 oz/yd2
(450 gsm)

126 in (3.2 m)

1.41 mm

10 years

15+ years

PVDF no grinding
needed

Open weave
mesh

.85 mm

10 years

Warranty, Duration

PVDF no grinding
needed

12+ years

UV Topcoat
Weight

UV Topcoat
Material

Life Expectancy

Coating

Weight
(Top, Bottom)

Yarn Count
(Warp, Fill)

Weave Style

Open weave
mesh

Trademark Holder/Supplier

Base Fabric

Low & Bonar
Coated Technical
Textiles
mehgies.com

Low & Bonar
Coated Technical
Textiles
mehgies.com

Trade Name of Fabric

Weight

Valmex FR TF 600

Valmex FR TF 400

Recommended Uses

Façade, shade
structures, tensile
architecture,
sound abatement

PVC Coated Polyester -
Weldable PVDF Coated

Façade, shade
structures, tensile
architecture,
sound abatement

PRODUCT

DIN 53363

DIN 53363

1200/1200 N

98.4 in, 118.1 in
(2.5 m, 3.0 m)

98.4 in, 118.1 in
(2.5 m, 3.0 m)
900/800 N

40 oz/yd2
(1350 gsm)

20 years

31 oz/yd2
(1050 gsm)

20 years

30+ years

Nano titanium
PVDF no grinding
needed

Nano titanium
PVDF no grinding
needed

30+ years

60/40

Modified Panama
3/3

60/40

Panama weave
2/2

Low & Bonar
Coated Technical
Textiles
mehgies.com

Valmex FR 1400
Nano, Type IV

Valmex FR 1000
Nano, Type III
Low & Bonar
Coated Technical
Textiles
mehgies.com

Tensile
architecture, long
term applications
medium-large
structures

Tensile
architecture, long
term applications
medium
structures

DIN 53363

2000/2000 N

98.4 in, 118.1 in
(2.5 m, 3.0 m)

45 oz/yd2
(1550 gsm)

20 years

30+ years

Nano titanium
PVDF no grinding
needed

60/40

Modified Panama
3/4

Low & Bonar
Coated Technical
Textiles
mehgies.com

Valmex FR 1600
Nano, Type V

Tensile
architecture,
long term
applications
small structures

DIN 53363

300/300 N

98.4 in, 118.1 in
(2.5 m, 3.0 m)

20.5 oz/yd2
(700 gsm)

20 years

30+ years

Nano titanium
PVDF no grinding
needed

60/40

Single Weave 1/1

Low & Bonar
Coated Technical
Textiles
mehgies.com

Valmex FR 700
Nano, Type I

Tensile
architecture,
long term
applications
small structures

DIN 53363

500/500 N

98.4 in, 118.1 in
(2.5 m, 3.0 m)

26.5 oz/yd2
(900 gsm)

20 years

30+ years

Nano titanium
PVDF no grinding
needed

60/40

Panama weave
2/2

Low & Bonar
Coated Technical
Textiles
mehgies.com

Valmex FR 900
Nano, Type II

Tensile
architecture,
long term
applications
small-medium
structures

PVC Coated Polyester - Weldable Nano PVDF Coating

DIN 53363

500/500 N

98.4 in, 118.1 in
(2.5 m, 3.0 m)

29.5 oz/yd2
(1000 gsm)

20 years

30+ years

Nano titanium
PVDF no grinding
needed

60/40

Panama weave
2/2

2 m, 78.5 in

990 g/m2

1.3 mm, 0.051 in

10 years

20 years

PVDF

Taffeta

990 g/m2

SEFAR
sefar.com

Sefar
Architecture
I/E 200-S

Valmex FR 900
Opaque Nano,
Type II
Low & Bonar
Coated Technical
Textiles
mehgies.com

Tension facades,
shading

Tensile
architecture,
permanent tent,
awning, air
supported

PVDF

52.8 in

2.01 oz/yd2

0.05 mm

20 years

2.01 oz/yd2
(50μm)

Denka
denka.co.jp

DX-Film

PVDF Film

AIR, TENT & TENSILE STRUCTURES

http://denka.co.jp http://www.sefar.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.mehgies.com http://www.FabricArchitectureMag.com